LAP100.29D4
LAP100.29D4 is suitable for production of high hardenability and high strength parts.

LAP100.29D4 is suitable for production of high hardenability and high strength parts.

Diffusion-alloyed powders are based on the atomized iron powders and reduced sponge iron powders have been diffusion bonded with certain content Mo, Ni, Cu. This type of materials make it possible to produce the parts with good performance after heat treatment.


图片 18.png 


The high compressibility of atomized iron powder makes it a perfect choice for manufacturing pure iron or iron alloy parts with high tensile strength as well as high compressive strength. The Water atomized iron powder is mainly used in powder metallurgy for production of high strength machine parts. Water atomized iron powder may be mixed with graphite,  nickel powder, copper powder and other metal powders to provide specific properties to the final product. It is also mixed with some lubricant such as zinc stearate before compaction.


图片 1.png


图片 19.png   图片 7.png


Specification of Atomized iron powder LAP100.29D4


Chemical Properties（%）

Unit

 Specification

Typical values


Min

Max

C

%


0.015

0.005

Si

%


0.05

0.03

Mn

%


0.15

0.10

P

%


0.015

0.011

S

%


0.015

0.005

Ni

%

1.40

1.60

1.52

Mo

%

0.50

0.70

0.58

Cu

%

1.80

2.20

1.93

HL

%


0.15

0.10

Physical Properties


Apparent density

g/cm3

3.00

3.30

3.05

Flow rate

s/50g


30.00

25.8

Green density 600Mpa

g/cm3

7.00


7.10

Particle size distribution（%）


180-212um

%


1

0

150-180um

%


10

1.8
106-150um%

20.8

75-106um

%

27.9

45-75um

%



28.6

-45um

%

15

30

20.9



PRODUCT PACKING

25kg/bag, 1000kg/bag, the package can be customized by buyer’s requirements.