LAP100.29D2
LAP100.29D2 is suitable for production of high hardenability and high strength parts.

LAP100.29D2 is suitable for production of high hardenability and high strength parts.

Diffusion-alloyed powders are based on the atomized iron powders and reduced sponge iron powders have been diffusion bonded with certain content Mo, Ni, Cu. This type of materials make it possible to produce the parts with good performance after heat treatment.


图片 18.png 


The high compressibility of atomized iron powder makes it a perfect choice for manufacturing pure iron or iron alloy parts with high tensile strength as well as high compressive strength. The Water atomized iron powder is mainly used in powder metallurgy for production of high strength machine parts. Water atomized iron powder may be mixed with graphite,  nickel powder, copper powder and other metal powders to provide specific properties to the final product. It is also mixed with some lubricant such as zinc stearate before compaction.


图片 1.png


图片 19.png   图片 7.png


Specification of Atomized iron powder LAP100.29D2


Chemical Properties（%）

Unit

                                    Specification



Min

Max

C

%


0.015

Si

%


0.05

Mn  

%


0.15

P

%


0.015

S

%


0.015

Ni

%

3.80

4.20

Mo

%

0.50

0.70

Cu

%

1.60

1.90

HL

%


0.15

Physical Properties

Apparent density

g/cm3

3.00

3.30

Flow rate

s/50g


30.00

Green density 600Mpa

g/cm3

7.06


Particle size distribution（%）

180-212um

%


1

150-180um

%


10

45-150um

%



-45um

%

10

30


PROPERTIES

LAP100.29D2+0.3%C+0.6%Zn-st, condition: temperature1120℃, sintering time 30min.


图片 4.png


图片 1_2.png  图片 2.png  图片 3.png


PRODUCT PACKING

25kg/bag, 1000kg/bag, the package can be customized by buyer’s requirements.


图片 8.png  图片 163.png